SMP800C compliant injection molding compound
Introduction
KYDEX® 2200IM is an injection moulding compound for use in mass transit interior applications where SMP800C or BSS7239 compliance is required.
General
Information
KYDEX® 2200IM meets the Federal Transit Administration (FTA) and the Federal Rail Administration (FRA) INFORMATION requirements for smoke emission and flammability as tested under ASTM E-662 and ASTM E-162. Additionally, KYDEX® 2200LT meets the toxicity criteria defined by SMP800C and BSS7239.
Suggested
Applications
- Trim pieces to cover seams or exposed edges when mating or joing parts
- Endcaps and snap fit covers
Features
- Meets flame-spread and smoke development requirements listed in 49 CFR 238
- Compliant to SMP800C and BSS7239 toxicity specifications
- Allows for tight tolerance control
- Sustainable: recycling eliminates disposal in landfill and associated costs.
PROCESSING CHARACTERISTICS
- Drying Temperature: 88°C (190°F)
- Drying Time: 3 – 4 Hours
- Process Temperature: 282°C (540°F)
- Contact SEKISUI KYDEX, LLC for more information.
ENVIRONMENTAL AND SAFETY CONSIDERATIONS
SEKISUI KYDEX®, LLC is committed to ensuring that its products can be manufactured, transported, stored, used, disposed and recycled with an appropriate regard for safety, health and environmental protection. We support the safe handling of our products. Please contact our Technical Service department at 800.682.8758 for resources or visit our website: http://www.kydex.com. For Material Safety Data Sheets, please call 800.325.3133.
| Property | Test Method | Typical Value1 | |
|---|---|---|---|
| PHYSICAL | |||
| Specific Gravity | ASTM D-792 | 1.30 | |
| Water Absorption, 24hr | ASTM D-570 | 0.10% | |
| Rockwell Hardness, R-Scale | ASTM D-785 | 111 | |
| MECHANICAL | |||
| Tensile Strength | ASTM D-638 | 52.7 MPa | 7,640 psi |
| Tensile Modulus | ASTM D-638 | 4,289 MPa | 622,000 psi |
| Flexural Strength | ASTM D-790 | 93.8 MPa | 13,600 psi |
| Flexural Modulus | ASTM D-790 | 4,275 MPa | 620,000 psi |
| Compressive Strength, yield | ASTM D-695 | 73.8 MPa | 10,700 psi |
| Compressive Modulus | ASTM D-695 | 4,268 MPa | 619,000 psi |
| Shear Strength | ASTM D-732 | 46.1 MPa | 6,690 psi |
| Bearing Strength, 4% deflection | ASTM D-953 | 41.7 MPa | 6,050 psi |
| Bearing Strength, max. | ASTM D-953 | 259.9 MPa | 37,700 psi |
| Notched Izod Impact | ASTM D-256 | 128.7 J/m | 2.41 ft-lb/inf |
| Gardner Drop Dart Impact, GE | ASTM D-5420 | 38.6 J | 342 in-lbf |
| Gardner Drop Dart Impact, GE @ -20°F (-29°C) | ASTM D-5420 | 16.3 J | 144 in-lb f |
| THERMAL | |||
| Heat Deflection Temperature (HDT) @ 1.8 MPa (264 psi) | ASTM D-648 | 82.2°C | 180°F |
| Heat Deflection Temperature (HDT) @ 0.455 MPa (66 psi) | ASTM D-648 | 90.3°C | 194.5°F |
| Coefficient of Thermal Expansion | ASTM E-831 | 49.2 µm/m/°C | 27.4 µin/in/°F |
| ELECTRICAL | |||
| Dielectric Strength, oil | ASTM D-149 | 18.6 > kV/mm | > 472 V/mil |
| FLAMMABILITY2 | |||
| Flammability:Flame Spread Index | ASTM E-162 | I <35 S No Burning Drip | |
| Flammability: Smoke Density | ASTM E-662 | D(1.5) <100 S D(4.0) <200 S | |
| Bombardier Toxic Gas Generation | SMP 800-C | Pass | |
| Boeing Toxic Gas Generation | BSS 7239 | Pass | |
| 1 Values based upon 3.18mm (0.125”) injection molded samples unless otherwise specified. 2 All Thicknesses and colours Not intended for specification purposes. | |||