Co-extruded, Medium Impact ABS, Medium Gloss Sheet
Introduction
ALLEN® 2090MG is a general purpose ABS that has medium impact strength, a medium gloss finish and a good cost to performance ratio to other materials like painted metal, FRP, aluminum, and other thermoplastics..
General
Information
ALLEN® 2090MG has been tested under laboratory conditions and has achieved a UL94 HB rating at 0.060 in (1.52mm) and above and meets the requirements of Federal Motor Vehicle Safety Standard No. 302 (FMVSS 302).
Suggested
Applications
- Covers and Housings
- Vehicle Interiors
- Office Furniture
- Displays
- Signs
Features
- Custom color matching
- Good forming properties
- Edge trim easily used into future orders
- UV protective films available
- Medium gloss finish
Environmental
& Safety
Considerations
SEKISUI KYDEX®, LLC is committed to ensuring that its products can be manufactured, transported, stored, used, disposed and recycled with an appropriate regard for safety, health and environmental protection. We support the safe handling of our products. Please contact our Technical Service department at 800.682.8758 for resources or visit our website: http://www.kydex.com. For Material Safety Data Sheets, please call 800.325.3133.
| Property | Test Method | Typical Value1 | |
|---|---|---|---|
| PHYSICAL | |||
| Specific Gravity | ASTM D792 | 1.06 g/cc | |
| Gloss, 60° Angle | ASTM D523 | 50 – 70% | |
| MECHANICAL | |||
| Tensile Strength, yield | ASTM D638 | 28.8 MPa | 4,170 psi |
| Flexural Stress at 5% Strain | ASTM D790 | 50.1 MPa | 7,270 psi |
| Flexural Modulus | ASTM D790 | 2,027 MPa | 294,000 psi |
| Notched Izod Impact Resistance, 73°F | ASTM D256 | 146 J/m | 2.74 ft-lbs/in |
| Notched Izod Impact Resistance, 0°F | ASTM D256 | 79 J/m | 1.49 ft-lbs/in |
| THERMAL | |||
| Heat Deflection Temperature (HDT) 66 psi (0.45 MPa), Unannealed | ASTM D648 | 96.5°C | 205.7°F |
| Mold Shrinkage | ASTM D955 | 0.005 – 0.007 in/in | |
| FLAMMABILITY | |||
| Motor Vehicle Safety Standard | Component Recognition | Pass | |
| 1 Values based upon injection molded resin Not intended for specification purposes. | |||