SMP800C compliant injection molding compound
Introduction
KYDEX® 2200IM is an injection moulding compound for use in mass transit interior applications where SMP800C or BSS7239 compliance is required.
General
Information
KYDEX® 2200IM meets the Federal Transit Administration (FTA) and the Federal Rail Administration (FRA) INFORMATION requirements for smoke emission and flammability as tested under ASTM E-662 and ASTM E-162. Additionally, KYDEX® 2200LT meets the toxicity criteria defined by SMP800C and BSS7239.
Suggested
Applications
- Trim pieces to cover seams or exposed edges when mating or joing parts
- APPLICATIONS • Endcaps and snap fit covers
Features
- Meets flame-spread and smoke development requirements listed in 49 CFR 238
- Compliant to SMP800C and BSS7239 toxicity specifications
- Allows for tight tolerance control
- Sustainable: recycling eliminates disposal in landfill and associated costs.
- PROCESSING • Drying Temperature: 88°C (190°F)
- CHARACTERISTICS • Drying Time: 3 – 4 Hours
- Process Temperature: 282°C (540°F)
- Contact SEKISUI KYDEX, LLC for more information.
- ENVIROMENTAL SEKISUI KYDEX, LLC is committed to ensuring that its products can be manufactured, transported, stored, used,
- AND SAFETY disposed and recycled with an appropriate regard for safety, health and environmental protection. We support the
Please contact our appLab™ department at 800.682.8758 for resources and Safety Data Sheets or visit our website: www.kydex.com.
| Property | Test Method | Typical Value1 | |
|---|---|---|---|
| PHYSICAL | |||
| Specific Gravity | ASTM D-792 | 1.30 | |
| Water Absorption, 24hr | ASTM D-570 | 0.10% | |
| Rockwell Hardness, R-Scale | ASTM D-785 | 111 | |
| MECHANICAL | |||
| Tensile Strength | ASTM D-638 | 52.7 MPa | 7,640 psi |
| Tensile Modulus | ASTM D-638 | 4,289 MPa | 622,000 psi |
| Flexural Strength | ASTM D-790 | 93.8 MPa | 13,600 psi |
| Flexural Modulus | ASTM D-790 | 4,275 MPa | 620,000 psi |
| Compressive Strength, yield | ASTM D-695 | 73.8 MPa | 10,700 psi |
| Compressive Modulus | ASTM D-695 | 4,268 MPa | 619,000 psi |
| Shear Strength | ASTM D-732 | 46.1 MPa | 6,690 psi |
| Bearing Strength, 4% deflection | ASTM D-953 | 41.7 MPa | 6,050 psi |
| Bearing Strength, max. | ASTM D-953 | 259.9 MPa | 37,700 psi |
| Notched Izod Impact | ASTM D-256 | 128.7 J/m | 2.41 ft-lb/in f |
| Gardner Drop Dart Impact, GE | ASTM D-5420 | 38.6 J | 342 in-lb f |
| Gardner Drop Dart Impact, GE @ -20°F (-29°C) | ASTM D-5420 | 16.3 J | 144 in-lb f |
| THERMAL | |||
| Heat Deflection Temperature (HDT) @ 1.8 MPa (264 psi) | ASTM D-648 | 82.2°C | 180°F |
| Heat Deflection Temperature (HDT) @ 0.455 MPa (66 psi) | ASTM D-648 | 90.3°C | 194.5°F |
| Coefficient of Thermal Expansion | ASTM E-831 | 49.2 µm/m/°C | 27.4 µin/in/°F |
| ELECTRICAL | |||
| Dielectric Strength, oil | ASTM D-149 | 18.6 > kV/mm | > 472 V/mil |
| FLAMMABILITY2 | |||
| Flammability:Flame Spread Index | ASTM E-162 | I <35 S No Burning Drip | |
| Flammability: Smoke Density | ASTM E-662 | D(1.5) <100 S D(4.0) <200 S | |
| Bombardier Toxic Gas Generation | SMP 800-C | Pass | |
| Boeing Toxic Gas Generation | BSS 7239 | Pass | |
| 1 Values based upon 3.18mm (0.125”) injection molded samples unless otherwise specified. 2 All Thicknesses and colours Not intended for specification purposes. | |||