Co-extruded, HighGloss ASA, Very High Impact PC/ABS
Introduction
ALLEN® 5200WHG Sheet has an excellent weatherable performance and property retention with high impact strength, high heat deflection, and stiffness.
General
Information
ALLEN® 5200WHG has been tested under laboratory conditions and has achieved a UL94 HB rating at 0.060 in INFORMATION (1.52mm) and above and meets the requirements of Federal Motor Vehicle Safety Standard No. 302 (FMVSS 302).
Suggested
Applications
- Engine Covers
- APPLICATIONS • Heavy Truck
- Recreational Vehicles
- Bus / Van
- Auto After-Market
- Agriculture / Construction Equiment
Features
- Wide range of colors
- Excellent physical property retention
- Good low temperature impact
- High heat deflection temperature
- Improved performance over ABS
- Higher modulus (Increased stiffness)
Environmental
& Safety
Considerations
SEKISUI KYDEX, LLC is committed to ensuring that its products can be manufactured, transported, stored, used, & SAFETY disposed and recycled with an appropriate regard for safety, health, and environmental protection. We support the safe handling of our products.
Please contact our appLab™ department at 800.682.8758 for resources and Safety Data Sheets or visit our website: www.kydex.com.
| Property | Test Method | Typical Value1 | |
|---|---|---|---|
| PHYSICAL | |||
| Specific Gravity | ASTM D792 | 1.13 | |
| Density | ASTM D792 | 1.13 g/cm3 | 0.041 lb/in3 |
| Water Absorption, equilibrium, 73oF | ASTM D570 | 0.17% | |
| Rockwell Hardness, R-scale | ASTM D785 | 111 | |
| MECHANICAL | |||
| Tensile Strength | ASTM D638 | 48.0 MPa | 6,960 psi |
| Tensile Modulus | ASTM D638 | 2096.0 MPa | 304,000 psi |
| Flexural Modulus | ASTM D790 | 2227.0 MPa | 323,000 psi |
| Flexural Stress at 5% Strain | ASTM D790 | 80.0 MPa | 11,600 psi |
| Compressive Strength, yield | ASTM D695 | 59.2 MPa | 8,590 psi |
| Shear Strength | ASTM D732 | 54.0 MPa | 7,830 psi |
| Bearing Strength, 4% deflection | ASTM D953 | 27.9 MPa | 4,040 psi |
| Bearing Strength, max. | ASTM D953 | 228.2 MPa | 33,100 psi |
| Notched Izod Impact Resistance @ 23°C (73°F) | ASTM D256 | 523.9 J/m | 9.81 ft-lbs/in |
| Notched Izod Impact Resistance @ -29°C (-20°F) | ASTM D256 | 438.3 J/m | 8.21 ft-lbs/in |
| Gardner Drop Dart Impact, GE @ 23°C (73°F) | ASTM D5420 | 50.1 J | 443 in-lb f |
| Gardner Drop Dart Impact, GE @ -29°C (-20°F) | ASTM D5420 | 59.0 J | 522 in-lb f |
| THERMAL | |||
| Heat Deflection Temperature (HDT) 264 psi (1.8 MPa), Unannealed | ASTM D648 | 101°C | 251.4°F |
| Heat Deflection Temperature (HDT) 66 psi (0.45 MPa), Unannealed | ASTM D648 | 122°C | 264.0°F |
| Coefficient of Thermal Expansion (TD) | ASTM E831 | 77 μm/m/°C | 42.8 μin/in/°F |
| ELECTRICAL | |||
| Dielectric Strength, oil | ASTM D149 | 21.7 kV/mm | 552 V/mil |
| FLAMMABILITY2 | |||
| Underwriters Laboratories., Inc ® Component Recognition | UL Standard 942 | HB @ 1.52mm (0.060 in) | |
| Motor Vehicle Safety Standard | FMVSS 302 | PASS | |
| 1 Values based upon 0.125” (3.17mm) sheet unless otherwise specified.. 2 ALLEN® 5200WHG has been tested under laboratory conditions and has passed UL 94HB criteria. SEKISUI KYDEX, LLC makes no warranty or guarantee that these products will meet UL 94HB in the part’s final, finished configuration. Not intended for specification purposes. | |||