Co-extruded, High Impact ABS, Low Gel, Medium Gloss Sheet
Introduction
ALLEN® 2015L is a general purpose ABS that has high impact strength and a good cost to performance ratio to other materials like painted metal, FRP, aluminum, and other thermoplastics.
General
Information
ALLEN® 2015L is low gel formulation for superior smooth surface and has been tested under laboratory conditions INFORMATION and has achieved a UL94 HB rating at 0.060 in (1.52mm) and above and meets the requirements of Federal Motor Vehicle Safety Standard No. 302 (FMVSS 302).
Suggested
Applications
- Marine products
- APPLICATIONS •Recreational Vehicles
- Agricultural cab interiors
- Truck interiors
- Equipment covers
- P.O.P Displays
- Film laminations
Features
- Ease of processing
- Regrind compatible in future orders
- Medium gloss finish
Environmental
& Safety
Considerations
SEKISUI KYDEX is committed to ensuring that its products can be manufactured, transported, stored, used, & SAFETY disposed and recycled with an appropriate regard for safety, health, and environmental protection. We support the safe handling of our products.
Please contact our appLab™ department at 800.682.8758 for resources and Safety Data Sheets or visit our website: www.kydex.com.
| Property | Test Method | Typical Value1 | |
|---|---|---|---|
| PHYSICAL | |||
| Specific Gravity | ASTM D792 | 1.06 | |
| Water Absorption, 24hr | ASTM D570 | 0.34 % | |
| Rockwell Hardness, R-Scale | ASTM D785 | 99 | |
| MECHANICAL | |||
| Tensile Strength | ASTM D638 | 5,950 psi | 41.0 MPa |
| Tensile Modulus | ASTM D638 | 287,000 psi | 1,978.8 MPa |
| Flexural Modulus | ASTM D790 | 289,000 psi | 1,993 MPa |
| Flexural Stress at 5% Strain | ASTM D790 | 9,390 psi | 64.7 MPa |
| Compressive Strength, yield | ASTM D695 | 7,210 psi | 49.7 MPa |
| Shear Strength | ASTM D732 | 5,400 psi | 37.2 MPa |
| Bearing Strength, 4% deflection | ASTM D953 | 3,030 psi | 20.9 MPa |
| Bearing Strength, max. | ASTM D953 | 26,500 psi | 182.7 MPa |
| Notched Izod Impact Resistance | ASTM D256 | 3.78 ft-lbs/in | 201.9 J/m |
| Gardner Drop Dart Impact, GE | ASTM D5420 | 213 in-lbf | 24.1 J |
| THERMAL | |||
| Heat Deflection Temperature (HDT) @264 psi (1.8 MPa), unannealed | ASTM D648 | 175 oF | 79.4 oC |
| Heat Deflection Temperature (HDT) @66 psi (0.45 MPa), unannealed | ASTM D648 | 195 oF | 90.6 oC |
| Coefficient of Thermal Expansion (MD) | ASTM E831 | 54.2 μin/in/oF | 97.5 μm/m/oC |
| ELECTRICAL | |||
| Dielectric Strength, oil | ASTM D149 | 497 V/mil | 19.6 kV/mm |
| FLAMMABILITY | |||
| Underwriters Laboratories., Inc ® Component Recognition | UL Standard 94 HB2 | HB @ 0.060 in (1.52mm) | |
| Motor Vehicle Safety Standard | FMVSS 302 | PASS | |
| 1 Values based upon 0.125” (3.17mm) sheet unless otherwise specified. 2 ALLEN® 2015L has been tested under laboratory conditions and has passed UL 94HB criteria. SEKISUI SPI makes no warranty or guarantee that these prod- ucts will meet UL 94HB in the part’s final, finished configuration. Not intended for specification purposes. | |||